Free sample Soft liquid silicone rubber for shoe insoles making

Orthopaedic Devices Casting Silicone

1. Description

G-808 A&B are two component silicone elastomers that crosslink at room temperature by polyaddition reaction. The polymerisation can be accelerated by heat. The silicone materials are delivered as two low viscous liquid components, which once mixed and cured, transform into an elastic and resistant material. Polymerisation occurs without formation of heat.

Tire Molding Silicone, Silicone Rubber for Tire Molding China, Silicone Rubber Mold Mix. GC RTV silicone G-8 series are great for tire molding. They have excellent tension and tear strength and flexibility, especially almost zero shrinkage. Best silicone rubber mold mix, silicone rubber for tire molding for hot sale.

2. Applications

Heel cushions,Toe separators,Liners for limb prostheses

3. Features

Very high stretch ability,Sterilisable,Low viscosity,Easy processing - mixing ratio 1 : 1

Technical Data

Characteristics of the non cured product

Properties	G-808
	A	B
Appearance	low viscous liquid
Colour	translucent
Density [g/cm 3 ] at 23 °C, approx	1.10
Viscosity [mPa·s] at 23 °C, approx	4000±1000

Polymerisation

Curing conditions: 1h at 80 °C

Properties	G-808
Hardness Shore A	8±2
Tensile strength [N/mm 2 ]	40±10
Elongation [%]	550±50
Tear strength [N/mm]	14±2

4.Processing

1. Mixing the two components The components A and B are mixed by weight in the above indicated ratio. The mixing can be carried out either by hand or using a low-speed electric or pneumatic mixer to minimise the introduction of air and to avoid any temperature increase. It is also possible to use a special mixing and dispensing machine for the two silicone components. Further information is available upon request.

2. Degassing The mixture should be degassed preferably at 30 to 50 mbar to eliminate any entrapped air. If a dispensing machine is used, the two components are degassed separately prior to mixing. The silicone mixture expands to 3 to 4 times of its initial volume and bubbles rise to the surface. The bubbles progressively disappear and the mixture returns to its initial volume after 5 to 10 minutes. Wait a few minutes to complete the degassing and then flash the vacuum. The silicone is ready for pouring, either by gravity or under low pressure. Note: Flashing the vacuum once or twice accelerates the degassing. It is recommended to use a container with a high diameter / height ratio.

3. Polymerisation The system polymerises at 23°C. The curing may be slowed down at lower temperature and contrary accelerated by heat. Contact with certain materials can inhibit the crosslinking. See list below:

• natural rubbers vulcanised with sulphur

• RTV 2 silicone elastomers catalysed with metal salts, e.g. tin-compounds

• PVC stabilised with tin salts and additives

• epoxy resins catalysed with amines

In case of doubts, it is recommended to test the substrate by applying a small quantity of the mixed silicone on a restricted area

5. Package

Part A:1kg/drum; 20kg/drum;25kg/drum;200kg/drum.

Part B:1kg/drum; 20kg/drum;25kg/drum;200kg/drum.

6. Storage and shelf life

When stored in their original unopened packaging, at a temperature of between -10°C and +30°C, the RTV GC-808 A & B can be stored for 12 months from the date of manufacture clearly marked on the packaging. Beyond this date, GC Silicone no longer guarantees that the products meet the sales specifications.