Supply rtv liquid silicone rubber making molds for art Foundry

Art & Foundry Casting Silicone Rubber

Model NO.: C-825 and C-830

Hardness: 25, 30 Shore A

Mixing Ratio: 100:2

Keyword: mold making silicone rubber, rtv 2 silicone rubber, liquid molding silicone

1.Description

silicone mold rubbers can also be used for wax, plaster and concrete casting, but are most beneficial for high volume resin or foam casting. Release agents are generally not needed for casting any of these materials, which is why they are sometimes preferred over polyurethanes. For resin sculptures that need to be painted after casting, silicone mold rubbers are recommended.

The popular silicone for these fields is C-825/C-830, medium hardness, tin-cured silicone rubber with a 100A:3B mix ratio (digital scale required for measuring) and 3-4hour demold time. Can easily be thickened with Liquid Thickener for brush-on application.

Guochuang Silicone Company manufacture and supply rtv 2 silicone rubber, RTV molding silicone rubber, silicone moulding rubber, 2 component silicon professionally. Our high quality architectural molding silicone, plaster molding silicone, rtv2 silicone for sale.

2. Technical Datasheet

Typical general characteristics	Inspection Method	Value
Product data (Catalyzed A+B)		C-825	C-830
Hardness	Shore A	25±2	30±2
Mix Ratio	A:B	100:3	100:3
Color	/	White	White
Pot life	25 °C (77F)	30-40mins	30-40mins
Curing time	25 °C (77F)	3-4 hours	3-4 hours
Mixed viscosity	mPa.s	20000±1000	23000±1000
Tear-strength	kg/cm	22±2	23±2
Tensile-strength	M.pa	4.0±0.5	5.0±0.5
Elongation	%	450±50	460±50
Shrinkage	%	≤0.3	≤0.3

Note: This is a 100A:3B mix ratio product that must be measured by weight. The choosing of suitable hardness should be according to the size and pattern design of the products. If large products and therefore multiple-piece molds are needed by customers, silicone rubber with higher hardness will be required for the molds. Conversely, soft silicon is indispensable for molds with complicated pattern and delicate details. The amount of curing agent admixture depends on the actual need of customers. More will be added for speedy drying and fast release and less when otherwise.

4. FEATURES

1.No oily surface on the cured mold

2.Low viscosity

3.Extra low shrinkage

4.Pouring and brushable silicone

5.High tear strength

6.various color is available

7.Heat Resistance(up to 180 degrees)

8.High reproduction rate

5.SHELF LIFE:

When stored at or below 32°C (89.6°F) in the original unopened containers, C-8 series Silicone Base and its Curing Agents have a usable life of I0 months.

6.Package

Silicone base:1kg/drum; 20kg/drum;25kg/drum;200kg/drum.

Curing Agent: 30g/bottle; 1kg/bottle